Protective plate

Product Type

Description

Physical and Chemical Data

Temperature of Application

Turbostops

Designed to prevent possible emergencies due to increased wear of the tundish working lining (gunite lining) in the area of the crucible and to reduce contamination with non-metallic inclusions
Turbostops are manufactured of low-cement corundum mass by vibratory casting.

-Al₂O₃, at least
80%

Fe₂O₃ not exceeding 1%,

-apparent porosity, not exceeding 20%,

-ultimate compressive strength after firing at t = 800C°

80-100 MPa

1,650-1,750 C°

Impact Plates

Designed to protect the steel-teeming ladle bottom against erosion by metal.

-apparent density at 110 Сº 2.6-3 g/cm³

-ultimate compressive strength at 110 °C, 30-70 N/mm²

depending on the raw material

Partitions

Used as protection at the metal jet impact point on the tundish bottom and walls. Partitions feature high erosion and corrosion resistance.