Protective plate

General Table

Product Type

Description

Physical and Chemical Data

Temperature of Application

Turbostops

Designed to prevent possible emergencies due to increased wear of the tundish working lining (gunite lining) in the area of the crucible and to reduce contamination with non-metallic inclusions
Turbostops are manufactured of low-cement corundum mass by vibratory casting.

-Al2O3, at least
80%

Fe2O3 not exceeding 1%,

-apparent porosity, not exceeding 20%,

-ultimate compressive strength after firing at t = 800C°

80-100 MPa

1,650-1,750 C°

Impact Plates

Designed to protect the steel-teeming ladle bottom against erosion by metal.

-apparent density at 110 Сº 2.6-3 g/cm3

-ultimate compressive strength at 110 °C, 30-70 N/mm2

depending on the raw material

Partitions

Used as protection at the metal jet impact point on the tundish bottom and walls. Partitions feature high erosion and corrosion resistance.

 

 

Concerning the acquisition of Slabs and obtaining detailed advice on product properties, delivery conditions and the conclusion of the contract, please contact the managers:

 

+74872701242

zakaz@vulkantm.com

Make a request

Fields marked with an asterisk (*) are required.








Thank you!

Application sent.
We will contact you shortly.

Make a request

Fields marked with an asterisk (*) are required.